JIS C3560 High Leaded Brass

JIS C3560 High Leaded Brass
JIS C3560 High Leaded Brass
Product Code : MAC 04
Brand Name : Mac
Product Description

By keeping track of the current market developments, we are involved in manufacturing, exporting and supplyingC34500 High Leaded Brass. This brass is used for armor in the outer walls and roofs of different architectural structures. Our offered brass is made available with us in numerous thickness, lengths and finishes. The provided brass is manufactured by our adroit professionals using superlative quality copper and zinc with the help of superior manufacturing techniques. Further, clients can avail this C34500 High Leaded Brass at market leading rates.

Features:

·         Durability

·         Corrosion resistance

·         Perfect finish

·         Stress crack proof

C34500 high leaded brass "64%" is the brass with high machining ability. The increase in lead content will result in increased machining ability with good strength and atmospheric corrosion resistance. The increased lead content will also provide pressure tightness by sealing the shrinkage pores.

Applications :

·         Industrial : Pinions, Gears, Valve Stems, Flare Fittings, Adapters, Couplings

·         Plumbing: Plumbing Fittings, Plumbers' Brass Goods

 

Equivalent Specifications:

CATEGORY / STANDARD

ASTM

BS

EN

JIS

DIN

ISO

High Leaded Brass

C34500

CZ131

CW601N

C3560

CuZn34Pb2

Specifications

Designation

ISO

CuZn34Pb2

Europen

CuZn35Pb2

JIS

C3560

Russian

LS63-2

Chemical Composition:

Cu

Fe

Pb

Zn

Min/Max

59.0-63.0

0.07

0.3

Rem

Nominals

60000

-0

-0

40

Specifications:

End Product

Specification

Bar

ASTM B36

Wire

ASTM B36

Rods

ASTM B36

Ingots

ASTM B36

Tube, Condenser

ASME SB111, ASTM B111

Tube, Seamless

ASTM B135, FEDERAL WW-T-791

Fabrication:

Joining Technique

Suitability

Brazing

Excellent

Butt Weld

Good

Capacity for Being Cold Worked

Fair

Capacity for Being Hot Formed

Excellent

Coated Metal Arc Welding

Not Recommended

Forgeability Rating

90

Gas Sheilded Arc Welding

Fair

Machinability rating

40

Oxyacetylene Welding

Good

Seam Weld

Not Recommended

Soldering

Excellent

Spot Weld

Good

Physical Properties:

Product Property

US Customary

Metric

Coefficient of Thermal Expansion

11.6 ·10-6 per oF (68-572 F)

20.9 · 10 6? per °C (20-300 C)

Density

0.303 lb/in3 @ 68 F

8.39 gm/cm3 @ 20 C

Electrical Conductivity

28 %IACS @ 68 F

0.164 MegaSiemens/cm @ 20 C

Electrical Resistivity

37.0 ohms-cmil/ft @ 68 F

6.15 microhm-cm @ 20 C

Melting Point Liquid US

1660 F

904 C

Melting Point Solid US

1650 F

899 C

Modulas of Elasticity in Tension

15000 ksi

103400 MPa

Modulas of Rigidity

5600 ksi

38610 MPa

Specific Gravity

8.39

8.39

Specific Heat Capacity

0.09 Btu/lb/°F @ 68 F

377.1 J/kg · °K at 293 K

Thermal Conductivity

71.0 Btu · ft/(hr · ft2 °F) @ 68 F

1229.9 W/m · °K at 20 C

Sizes Available

WIRE

1mm TO 8 mm

HOLLOW RODS

Min Bore Size 20 mm and Max OD 100 mm

ROUND RODS

6mm To 130 mm

HEX

5mm To 60mm

SQUARE

4mm To 60mm

FLAT

5mm Min Thickness and max Width 120mm

PROFILES / SECTIONS

AS per Customer Drawing

BILLETS

Up to 200mm

INGOTS

AS per Specification

 

 


METAL ALLOYS CORPORATION

Contact Us

( *represents compulsory fields )

Tips on getting accurate quotes. Please include product name, order quantity, usage, special requests if any in your inquiry.



METAL ALLOYS CORPORATION All Rights Reserved.